Product Information
Composition of Super Austenitic N08811 Pipe and Tubing
| Grade | N08811 |
|---|
| UNS Designation | N08811 |
|---|
| Nickel (Ni) |
30.0– 35.0 |
| Chromium (Cr) |
19.0–23.0 |
| Iron (Fe) |
39.5 Min. |
| Molybdenum (Mo) |
— |
| Titanium (Ti) Max. |
0.15–0.60* |
| Aluminum (Al) Max. |
0.15–0.60 |
| Cobalt (Co) Max. |
— |
| Tungsten (W) |
— |
| Vanadium (V) Max. |
— |
| Copper (Cu) Max. |
0.75 |
| Manganese (Mn) Max. |
1.5 |
| Niobium (Nb) plus Tantalum |
— |
| Carbon (C) Max. |
0.06–0.10 |
| Nitrogen (N) Max. |
— |
| Silicon (Si) Max. |
100 |
| Sulphur (S) Max. |
0.1015 |
| Phosphorous (P) Max. |
— |
| Other Elements |
— |
Physical Properties of Super Austenitic N08811 Alloy in the Annealed Condition at -20°F to +100°F
| Â |
 |
 |
Tensile Strength | Yield Strength |
 |
 |
 |
 |
 |
 |
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
|---|
| 800HT |
N08811 |
B514, B515 |
65,000 |
450 |
65 |
25,000 |
170 |
25 |
30 |
5 & coarser |
— |
— |
7.9 |
80 |
Super Austenitic N08811 Product Range
| UNS Designation | Werkstoff NR. | Specifications* |
|---|
| N08811 |
1.4876 |
B/SB515, B/SB514 |
*Note: The specifications noted including ASTM, ASME, or other applicable authorities are correct at the time of publication. Other specifications may apply for use of these materials in different applications.