444
Composition of Pipe and Tubing
| Grade | 444 |
|---|
| UNS Designation | S44400 |
|---|
| Nickel (Ni) |
1.00 |
| Chromium (Cr) |
17.5–19.5 |
| Iron (Fe) |
Bal. |
| Molybdenum (Mo) |
1.75–2.50 |
| Titanium (Ti) Max. |
0.20 + 4x (C + N) Min. to 0.80 Max. |
| Aluminum (Al) Max. |
— |
| Cobalt (Co) Max. |
— |
| Tungsten (W) |
— |
| Vanadium (V) Max. |
— |
| Copper (Cu) Max. |
— |
| Manganese (Mn) Max. |
1.00 |
| Niobium (Nb) plus Tantalum |
— |
| Carbon (C) Max. |
0.025 |
| Nitrogen (N) Max. |
0.035 |
| Silicon (Si) Max. |
1.00 |
| Sulphur (S) Max. |
0.030 |
| Phosphorous (P) Max. |
0.040 |
| Other Elements |
— |
444
Physical Properties in the Annealed Condition at -20°F to +100°F
| | | | Tensile Strength | Yield Strength | | | | | | |
|---|
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
|---|
| 444 |
S44400 |
A268 |
60,000 |
415 |
60 |
40,000 |
275 |
40 |
12* |
— |
100 Rb |
— |
7.7 |
186 |
444
Product Range
| Alloy | UNS Designation | Werkstoff NR. | Specifications* |
|---|
| 444 |
S44400 |
N/A |
A/SA268 |
*Note: The specifications noted including ASTM, ASME, or other applicable authorities are correct at the time of publication. Other specifications may apply for use of these materials in different applications.