309S/309H
Composition of Pipe and Tubing
| Grade | 309S | 309H |
|---|
| UNS Designation | S30908 | S30909 |
|---|
| Carbon (C) Max. |
0.08 |
0.04–0.10 |
| Manganese (Mn) Max. |
2.00 |
2.00 |
| Phosphorous (P) Max. |
0.045 |
0.045 |
| Sulphur (S) Max. |
0.030 |
0.030 |
| Silicon (Si) Max. |
1.00 |
1.00 |
| Chromium (Cr) |
22.0–24.0 |
22.0–24.0 |
| Nickel (Ni) |
12.0–15.0 |
12.0–15.0 |
| Molybdenum (Mo) |
— |
— |
| Nitrogen (N) |
— |
— |
| Iron (Fe) |
Bal. |
Bal. |
| Other Elements |
— |
— |
309S/309H
Physical Properties in the Annealed Condition at -20°F to +100°F
| | | | Tensile Strength | Yield Strength | | | | | | |
|---|
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Maximum Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) |
|---|
| 309S |
S30908 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
— |
90 Rb |
29.0 |
9.2 |
116 |
| 309H |
S30909 |
— |
75,000 |
515 |
— |
30,000 |
205 |
— |
35 |
6 or coarser |
— |
29.0 |
9.2 |
— |
309S/309H
Product Range
| Alloy | UNS Designation | Werkstoff NR. | Specifications* |
|---|
| 309S |
S30908 |
1.4833 |
A/SA249, A/SA312 |
| 309H |
S30909 |
1.4306 |
A/SA249, A/SA312 |
*Note: The specifications noted including ASTM, ASME, or other applicable authorities are correct at the time of publication. Other specifications may apply for use of these materials in different applications.